比重
|
1.46
|
|
ASTM D792
|
|
特定体积
|
19.1
|
in³/lb
|
ASTM D792
|
|
收缩率
|
|
|
内部方法
|
|
流动 3
|
6.0E-3 到 8.0E-3
|
in/in
|
|
|
流动 : 0.126 in
|
8.0E-3 到 0.010
|
in/in
|
|
|
横向流动 3
|
6.0E-3 到 8.0E-3
|
in/in
|
|
|
横向流动 : 0.126 in
|
8.0E-3 到 0.010
|
in/in
|
|
|
吸水率 (24 hr)
|
0.090
|
%
|
ASTM D570
|
|
洛氏硬度 (R 级)
|
112
|
|
ASTM D785
|
|
抗张强度 4
|
|
|
ASTM D638
|
|
屈服
|
7100
|
psi
|
|
|
断裂
|
6800
|
psi
|
|
|
弯曲模量 5 (1.97 in 跨距)
|
500000
|
psi
|
ASTM D790
|
|
弯曲强度 5 (屈服, 1.97 in 跨距)
|
13000
|
psi
|
ASTM D790
|
|
悬壁梁缺口冲击强度 (73°F)
|
1.5
|
ft·lb/in
|
ASTM D256
|
|
无缺口悬臂梁冲击 (73°F)
|
30
|
ft·lb/in
|
ASTM D4812
|
|
载荷下热变形温度
|
|
|
ASTM D648
|
|
66 psi, 未退火, 0.252 in
|
320
|
°F
|
|
|
264 psi, 未退火, 0.252 in
|
190
|
°F
|
|
|
线形热膨胀系数 - 流动
|
|
|
ASTM E831
|
|
-40 到 104°F
|
4.2E-5
|
in/in/°F
|
|
|
140 到 280°F
|
7.7E-5
|
in/in/°F
|
|
|
RTI Elec
|
221
|
°F
|
UL 746
|
|
RTI Imp
|
221
|
°F
|
UL 746
|
|
RTI
|
221
|
°F
|
UL 746
|
|
体积电阻率
|
6.9E+16
|
ohms·cm
|
ASTM D257
|
|
介电强度
|
|
|
ASTM D149
|
|
0.0630 in, in Oil
|
630
|
V/mil
|
|
|
0.126 in, in Air
|
590
|
V/mil
|
|
|
介电常数
|
|
|
ASTM D150
|
|
100 Hz
|
3.30
|
|
|
|
1 MHz
|
3.20
|
|
|
|
耗散因数
|
|
|
ASTM D150
|
|
100 Hz
|
2.0E-3
|
|
|
|
1 MHz
|
0.014
|
|
|
|
耐电弧性 6
|
PLC 5
|
|
ASTM D495
|
|
相比耐漏电起痕指数(CTI)
|
PLC 2
|
|
UL 746
|
|
高电弧燃烧指数(HAI)
|
PLC 0
|
|
UL 746
|
|
高电压电弧起痕速率 (HVTR)
|
PLC 3
|
|
UL 746
|
|
热丝引燃 (HWI)
|
PLC 2
|
|
UL 746
|
|
UL 阻燃等级 (0.0580 in)
|
HB
|
|
UL 94
|
|
干燥温度
|
250
|
°F
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
12
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 80
|
%
|
|
|
料筒后部温度
|
470 到 490
|
°F
|
|
|
料筒中部温度
|
480 到 500
|
°F
|
|
|
料筒前部温度
|
490 到 510
|
°F
|
|
|
射嘴温度
|
490 到 520
|
°F
|
|
|
加工（熔体）温度
|
490 到 530
|
°F
|
|
|
模具温度
|
150 到 200
|
°F
|
|
|
背压
|
50.0 到 100
|
psi
|
|
|
螺杆转速
|
50 到 80
|
rpm
|
|
|
排气孔深度
|
1.0E-3 到 1.5E-3
|
in
|
|
|