比重
|
|
|
|
|
--
|
1.34
|
|
ASTM D792
|
|
--
|
1.34
|
g/cm³
|
ISO 1183
|
|
熔流率（熔体流动速率）
|
|
|
ASTM D1238
|
|
250°C/5.0 kg
|
9.6
|
g/10 min
|
|
|
265°C/5.0 kg
|
13
|
g/10 min
|
|
|
266°C/5.0 kg
|
13
|
g/10 min
|
|
|
溶化体积流率（MVR）
|
|
|
ISO 1133
|
|
250°C/5.0 kg
|
0.488
|
in³/10min
|
|
|
265°C/5.0 kg
|
0.610
|
in³/10min
|
|
|
收缩率
|
|
|
内部方法
|
|
流动 3
|
0.011 到 0.018
|
in/in
|
|
|
流动 : 0.126 in
|
0.010 到 0.014
|
in/in
|
|
|
横向流动 3
|
9.0E-3 到 0.018
|
in/in
|
|
|
吸水率
|
|
|
ISO 62
|
|
饱和, 73°F
|
0.50
|
%
|
|
|
平衡, 73°F, 50% RH
|
0.15
|
%
|
|
|
洛氏硬度 (R 计秤)
|
115
|
|
ISO 2039-2
|
|
球压硬度 (H 358/30)
|
16700
|
psi
|
ISO 2039-1
|
|
拉伸模量
|
|
|
|
|
-- 4
|
290000
|
psi
|
ASTM D638
|
|
--
|
319000
|
psi
|
ISO 527-2/1
|
|
抗张强度
|
|
|
|
|
屈服 5
|
7250
|
psi
|
ASTM D638
|
|
屈服
|
7250
|
psi
|
ISO 527-2/50
|
|
断裂 5
|
5800
|
psi
|
ASTM D638
|
|
断裂
|
5800
|
psi
|
ISO 527-2/50
|
|
伸长率
|
|
|
|
|
屈服 5
|
5.0
|
%
|
ASTM D638
|
|
屈服
|
5.0
|
%
|
ISO 527-2/50
|
|
断裂 5
|
30
|
%
|
ASTM D638
|
|
断裂
|
30
|
%
|
ISO 527-2/50
|
|
弯曲模量
|
|
|
|
|
1.97 in 跨距 6
|
305000
|
psi
|
ASTM D790
|
|
-- 7
|
290000
|
psi
|
ISO 178
|
|
弯曲应力
|
|
|
|
|
-- 7, 8
|
11600
|
psi
|
ISO 178
|
|
屈服, 1.97 in 跨距 6
|
11300
|
psi
|
ASTM D790
|
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮)
|
33.0
|
mg
|
内部方法
|
|
简支梁缺口冲击强度
|
|
|
|
|
-22°F 9
|
9.5
|
ft·lb/in²
|
ISO 179/1eA, ISO 179/2C
|
|
73°F 9
|
21
|
ft·lb/in²
|
ISO 179/1eA
|
|
73°F
|
19
|
ft·lb/in²
|
ISO 179/2C
|
|
简支梁无缺口冲击强度 9
|
|
|
ISO 179/1eU, ISO 179/2U
|
|
-22°F
|
无断裂
|
|
|
|
73°F
|
无断裂
|
|
|
|
悬壁梁缺口冲击强度
|
|
|
|
|
-22°F
|
2.8
|
ft·lb/in
|
ASTM D256
|
|
32°F
|
3.6
|
ft·lb/in
|
ASTM D256
|
|
73°F
|
9.4
|
ft·lb/in
|
ASTM D256
|
|
-22°F 10
|
4.8
|
ft·lb/in²
|
ISO 180/1A
|
|
32°F 10
|
9.5
|
ft·lb/in²
|
ISO 180/1A
|
|
73°F 10
|
19
|
ft·lb/in²
|
ISO 180/1A
|
|
无缺口悬臂梁冲击
|
|
|
ASTM D4812, ISO 180/1U
|
|
-22°F
|
无断裂
|
|
|
|
73°F
|
无断裂
|
|
|
|
装有测量仪表的落镖冲击 (73°F, Total Energy)
|
310
|
in·lb
|
ASTM D3763
|
|
载荷下热变形温度
|
|
|
|
|
66 psi, 未退火, 0.126 in
|
266
|
°F
|
ASTM D648
|
|
66 psi, 未退火, 3.94 in 跨距 11
|
275
|
°F
|
ISO 75-2/Be
|
|
66 psi, 未退火, 2.52 in 跨距 12
|
266
|
°F
|
ISO 75-2/Bf
|
|
264 psi, 未退火, 0.126 in
|
185
|
°F
|
ASTM D648
|
|
264 psi, 未退火, 3.94 in 跨距 11
|
185
|
°F
|
ISO 75-2/Ae
|
|
264 psi, 未退火, 2.52 in 跨距 12
|
185
|
°F
|
ISO 75-2/Af
|
|
维卡软化温度
|
|
|
|
|
--
|
293
|
°F
|
ASTM D1525 13, ISO 306/B50 13
|
|
--
|
356
|
°F
|
ASTM D1525 14, ISO 306/A50 14
|
|
--
|
302
|
°F
|
ISO 306/B120
|
|
Ball Pressure Test (257°F)
|
Pass
|
|
IEC 60695-10-2
|
|
线形热膨胀系数
|
|
|
|
|
流动 : -40 到 104°F
|
5.1E-5
|
in/in/°F
|
ASTM E831
|
|
流动 : 73 到 176°F
|
5.6E-5
|
in/in/°F
|
ISO 11359-2
|
|
横向 : -40 到 104°F
|
4.7E-5
|
in/in/°F
|
ASTM E831
|
|
横向 : 73 到 176°F
|
5.6E-5
|
in/in/°F
|
ISO 11359-2
|
|
导热系数
|
1.2
|
Btu·in/hr/ft²/°F
|
ISO 8302
|
|
RTI Elec
|
248
|
°F
|
UL 746
|
|
RTI Imp
|
248
|
°F
|
UL 746
|
|
RTI
|
284
|
°F
|
UL 746
|
|
表面电阻率
|
> 1.0E+15
|
ohms
|
IEC 60093
|
|
体积电阻率
|
> 1.0E+15
|
ohms·cm
|
ASTM D257, IEC 60093
|
|
介电强度
|
|
|
|
|
0.0630 in, in Oil
|
640
|
V/mil
|
ASTM D149
|
|
0.126 in, in Oil
|
430
|
V/mil
|
ASTM D149
|
|
0.0315 in, 在油中
|
860
|
V/mil
|
IEC 60243-1
|
|
0.0630 in, 在油中
|
640
|
V/mil
|
IEC 60243-1
|
|
0.126 in, 在油中
|
430
|
V/mil
|
IEC 60243-1
|
|
介电常数
|
|
|
|
|
1 MHz
|
3.00
|
|
ASTM D150, IEC 60250
|
|
50 Hz
|
3.00
|
|
IEC 60250
|
|
60 Hz
|
3.00
|
|
IEC 60250
|
|
耗散因数
|
|
|
|
|
1 MHz
|
0.013
|
|
ASTM D150
|
|
50 Hz
|
2.0E-3
|
|
IEC 60250
|
|
60 Hz
|
2.0E-3
|
|
IEC 60250
|
|
1 MHz
|
1.3E-3
|
|
IEC 60250
|
|
耐电弧性 15
|
PLC 6
|
|
ASTM D495
|
|
相比耐漏电起痕指数(CTI)
|
PLC 3
|
|
UL 746
|
|
漏电起痕指数
|
|
|
IEC 60112
|
|
--
|
225
|
V
|
|
|
解决方案 B
|
100
|
V
|
|
|
高电弧燃烧指数(HAI)
|
PLC 0
|
|
UL 746
|
|
高电压电弧起痕速率 (HVTR)
|
PLC 3
|
|
UL 746
|
|
热丝引燃 (HWI)
|
PLC 3
|
|
UL 746
|
|
UL 阻燃等级
|
|
|
UL 94
|
|
0.0295 in
|
V-0
|
|
|
|
0.0984 in
|
5VA
|
|
|
|
灼热丝易燃指数 (0.0394 in)
|
1760
|
°F
|
IEC 60695-2-12
|
|
极限氧指数
|
30
|
%
|
ISO 4589-2
|
|
熔体粘度 (500°F, 1500 sec^-1)
|
310
|
Pa·s
|
ISO 11443
|
|
干燥温度
|
230 到 248
|
°F
|
|
|
干燥时间
|
2.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
料斗温度
|
104 到 140
|
°F
|
|
|
料筒后部温度
|
446 到 473
|
°F
|
|
|
料筒中部温度
|
464 到 491
|
°F
|
|
|
料筒前部温度
|
473 到 509
|
°F
|
|
|
射嘴温度
|
464 到 500
|
°F
|
|
|
加工（熔体）温度
|
482 到 518
|
°F
|
|
|
模具温度
|
104 到 212
|
°F
|
|
|