比重
|
|
|
ASTM D792
|
|
--
|
1.21
|
|
|
|
--
|
1.22
|
g/cm³
|
|
|
特定体积
|
23.1
|
in³/lb
|
ASTM D792
|
|
熔流率（熔体流动速率） (300°C/1.2 kg)
|
10
|
g/10 min
|
ASTM D1238
|
|
收缩率 - 流动 (0.126 in)
|
5.0E-3 到 7.0E-3
|
in/in
|
内部方法
|
|
吸水率
|
|
|
ASTM D570
|
|
24 hr
|
0.15
|
%
|
|
|
平衡, 73°F
|
0.35
|
%
|
|
|
平衡, 212°F
|
0.58
|
%
|
|
|
室外适用性
|
f1
|
|
UL 746C
|
|
洛氏硬度
|
|
|
ASTM D785
|
|
M 级
|
70
|
|
|
|
R 级
|
118
|
|
|
|
抗张强度 3
|
|
|
ASTM D638
|
|
屈服
|
9000
|
psi
|
|
|
断裂
|
8100
|
psi
|
|
|
伸长率 3
|
|
|
ASTM D638
|
|
屈服
|
7.0
|
%
|
|
|
断裂
|
90
|
%
|
|
|
弯曲模量 4 (1.97 in 跨距)
|
325000
|
psi
|
ASTM D790
|
|
弯曲强度 4 (屈服, 1.97 in 跨距)
|
13200
|
psi
|
ASTM D790
|
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮)
|
10.0
|
mg
|
ASTM D1044
|
|
悬壁梁缺口冲击强度 (73°F)
|
12
|
ft·lb/in
|
ASTM D256
|
|
无缺口悬臂梁冲击 (73°F)
|
60
|
ft·lb/in
|
ASTM D4812
|
|
落锤冲击 (73°F)
|
1500
|
in·lb
|
ASTM D3029
|
|
拉伸冲击强度 5
|
250
|
ft·lb/in²
|
ASTM D1822
|
|
载荷下热变形温度
|
|
|
ASTM D648
|
|
66 psi, 未退火, 0.252 in
|
280
|
°F
|
|
|
264 psi, 未退火, 0.252 in
|
270
|
°F
|
|
|
维卡软化温度
|
305
|
°F
|
ASTM D1525 6
|
|
线形热膨胀系数 - 流动 (-40 到 203°F)
|
3.8E-5
|
in/in/°F
|
ASTM E831
|
|
导热系数
|
1.3
|
Btu·in/hr/ft²/°F
|
ASTM C177
|
|
RTI Elec
|
266
|
°F
|
UL 746
|
|
RTI Imp
|
248
|
°F
|
UL 746
|
|
RTI
|
266
|
°F
|
UL 746
|
|
体积电阻率
|
> 1.0E+17
|
ohms·cm
|
ASTM D257
|
|
介电强度 (0.126 in, in Air)
|
430
|
V/mil
|
ASTM D149
|
|
介电常数
|
|
|
ASTM D150
|
|
50 Hz
|
3.01
|
|
|
|
60 Hz
|
3.01
|
|
|
|
1 MHz
|
2.96
|
|
|
|
耗散因数
|
|
|
ASTM D150
|
|
50 Hz
|
9.0E-4
|
|
|
|
60 Hz
|
9.0E-4
|
|
|
|
1 MHz
|
0.010
|
|
|
|
耐电弧性 7
|
PLC 7
|
|
ASTM D495
|
|
相比耐漏电起痕指数(CTI)
|
PLC 2
|
|
UL 746
|
|
高电弧燃烧指数(HAI)
|
PLC 3
|
|
UL 746
|
|
高电压电弧起痕速率 (HVTR)
|
PLC 3
|
|
UL 746
|
|
热丝引燃 (HWI)
|
PLC 2
|
|
UL 746
|
|
UL 阻燃等级 (0.0430 in)
|
V-0
|
|
UL 94
|
|
极限氧指数
|
35
|
%
|
ASTM D2863
|
|
Radiant Panel Listing (UL)
|
YES
|
|
|
|
干燥温度
|
250
|
°F
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
520 到 560
|
°F
|
|
|
料筒中部温度
|
540 到 580
|
°F
|
|
|
料筒前部温度
|
560 到 600
|
°F
|
|
|
射嘴温度
|
550 到 590
|
°F
|
|
|
加工（熔体）温度
|
560 到 600
|
°F
|
|
|
模具温度
|
160 到 200
|
°F
|
|
|
背压
|
50.0 到 100
|
psi
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
1.0E-3 到 3.0E-3
|
in
|
|
|