比重
|
1.52
|
g/cm³
|
ASTM D792
|
|
特定体积
|
0.658
|
cm³/g
|
ASTM D792
|
|
熔流率（熔体流动速率） (300°C/5.0 kg)
|
13
|
g/10 min
|
ASTM D1238
|
|
收缩率 - 流动 (3.20 mm)
|
0.10 到 0.20
|
%
|
内部方法
|
|
吸水率
|
|
|
ASTM D570
|
|
24 hr
|
0.12
|
%
|
|
|
平衡, 23°C
|
0.23
|
%
|
|
|
洛氏硬度
|
|
|
ASTM D785
|
|
M 级
|
93
|
|
|
|
R 级
|
119
|
|
|
|
抗张强度 3 (断裂)
|
125
|
MPa
|
ASTM D638
|
|
伸长率 3 (断裂)
|
3.0
|
%
|
ASTM D638
|
|
弯曲模量 4 (50.0 mm 跨距)
|
9650
|
MPa
|
ASTM D790
|
|
弯曲强度 4 (屈服, 50.0 mm 跨距)
|
186
|
MPa
|
ASTM D790
|
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮)
|
32.0
|
mg
|
ASTM D1044
|
|
悬壁梁缺口冲击强度 (23°C)
|
130
|
J/m
|
ASTM D256
|
|
无缺口悬臂梁冲击 (23°C)
|
1300
|
J/m
|
ASTM D4812
|
|
落锤冲击 (23°C)
|
6.78
|
J
|
ASTM D3029
|
|
拉伸冲击强度 5
|
67.2
|
kJ/m²
|
ASTM D1822
|
|
载荷下热变形温度
|
|
|
ASTM D648
|
|
0.45 MPa, 未退火, 6.40 mm
|
154
|
°C
|
|
|
1.8 MPa, 未退火, 6.40 mm
|
146
|
°C
|
|
|
维卡软化温度
|
166
|
°C
|
ASTM D1525 6
|
|
线形热膨胀系数 - 流动 (-40 到 95°C)
|
1.6E-5
|
cm/cm/°C
|
ASTM E831
|
|
比热
|
1050
|
J/kg/°C
|
ASTM C351
|
|
导热系数
|
0.22
|
W/m/K
|
ASTM C177
|
|
RTI Elec
|
130
|
°C
|
UL 746
|
|
RTI Imp
|
130
|
°C
|
UL 746
|
|
RTI
|
130
|
°C
|
UL 746
|
|
体积电阻率
|
> 1.0E+17
|
ohms·cm
|
ASTM D257
|
|
介电强度 (3.20 mm, in Air)
|
18
|
kV/mm
|
ASTM D149
|
|
介电常数
|
|
|
ASTM D150
|
|
50 Hz
|
3.53
|
|
|
|
60 Hz
|
3.53
|
|
|
|
1 MHz
|
3.48
|
|
|
|
耗散因数
|
|
|
ASTM D150
|
|
50 Hz
|
1.3E-3
|
|
|
|
60 Hz
|
1.3E-3
|
|
|
|
1 MHz
|
6.7E-3
|
|
|
|
耐电弧性 7
|
PLC 7
|
|
ASTM D495
|
|
相比耐漏电起痕指数(CTI)
|
PLC 4
|
|
UL 746
|
|
高电弧燃烧指数(HAI)
|
PLC 4
|
|
UL 746
|
|
高电压电弧起痕速率 (HVTR)
|
PLC 3
|
|
UL 746
|
|
热丝引燃 (HWI)
|
PLC 0
|
|
UL 746
|
|
UL 阻燃等级
|
|
|
UL 94
|
|
1.12 mm
|
V-1
|
|
|
|
3.00 mm
|
V-0
|
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
293 到 316
|
°C
|
|
|
料筒中部温度
|
304 到 327
|
°C
|
|
|
料筒前部温度
|
316 到 338
|
°C
|
|
|
射嘴温度
|
310 到 332
|
°C
|
|
|
加工（熔体）温度
|
316 到 338
|
°C
|
|
|
模具温度
|
82.2 到 116
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
|
|